Thermodynamic studies in the MgO – FeO – Al2O3 system

  • O. M. Borysenko Simon Kuznets Kharkiv National University of Economics, Kharkiv, Ukraine
  • S. M. Logvinkov Simon Kuznets Kharkiv National University of Economics, Kharkiv, Ukraine
  • G. M. Shabanova NTU "Kharkov Polytechnic Institute", Kharkiv, Ukraine
  • A. M. Korohodska NTU "Kharkov Polytechnic Institute", Kharkiv, Ukraine
  • I. A. Ostapenko TOV "Druzhkivskiy Vognetrivkiy zavod", Druzhkivka, Ukraine
  • A. A. Ivashura Simon Kuznets Kharkiv National University of Economics, Kharkiv, Ukraine
Keywords: refractory materials, alumina magnesia spinel, hercinite, Gibbs energy change, system triangulation.

Abstract

Prediction of the phase composition is one of the most important tasks in the development of new refractory materials and their operation in thermal units. The most complete information on phase interactions and thermodynamic stability of phase combinations is contained in the phase diagrams.

The article presents thermodynamic studies of the three - component system MgO – FeO – Al2O3, which is of great interest for the production of refractory materials with high performance characteristics. Based on the analysis of binary systems of this system, it was found that, the stable phases are MgO, FeO, Al2O3 and MgAl2O4, FeAl2O4. The results analysis of calculating the Gibbs energy for the reaction (FeO + MgAl2O4 = MgO + FeAl2O4) indicates the thermodynamic stability of the phases combination of MgO, FeAl2O4 to a temperature of 1141 K. Above the temperature of 1141 K FeO and MgAl2O4 are stable phases. Thus, in the system MgO – FeO – Al2O3 up to the temperature of 1141 K, the phases MgO – FeAl2O4 and MgAl2O4 – FeAl2O4 coexist, above this temperature — FeO – MgAl2O4 and MgAl2O4 – FeAl2O4.

The data obtained make it possible to predict thermally stimulated phase changes that give the effect of thermoplasticity and will be important for obtaining refractory materials with high performance characteristics based on the MgO — FeO — Al2O3 system.

References

Самойлова О. В., Макровец Л. А. Термодинамическое моделирование фазовых диаграмм оксидных систем FeO – MgO, FeO – Cr2O3, MgO – Cr2O3 и FeO – MgO – Cr2O3. Вестник ЮУрГУ. Сер. Металлургия. 2019. № 1, т. 19. С. 18—25.

Samoylova O. V., Makrovets L. A. Termodinamicheskoye modelirovaniye fazovykh diagramm oksidnykh sistem FeO – MgO, FeO – Cr2O3, MgO – Cr2O3 i FeO – MgO – Cr2O3 [Thermodynamic modeling of phase diagrams of oxide systems FeO – MgO, FeO – Cr2O3, MgO – Cr2O3 i FeO – MgO – Cr2O3]. Vestnik YUUrGU. Ser.: Metallurgiya [Bulletin of the South Ural State University. Series: Metallurgy]. 2019, vol. 19, no. 1, рр. 18—25 (in Russian).

Бережной А. С. Многокомпонентные системы окислов. Киев : Наук. думка, 1970. 544 с.

Berezhnoy A. S. Mnogokomponentnyye sistemy okislov [Multicomponent oxide systems]. Кyiv, Nauk. dumka Publ., 1970. 544 р. (in Russian).

Thermodynamic modelling of the Al2O3 – CaO – FeO – Fe2O3 – PbO – SiO2 – ZnO system with addition of K and Na with metallurgical applications / E. Jak, P. Hayes., A. Pelton., S. Decterov. Santiago, Chile, 2009. P. 473—490. URL: https://pdfs.semanticscholar.org/0804/0a0bc1ea0e1f5a0ca22d7b78e3ad3e2a191d.pdf.

Jak E., Hayes P., Pelton A., Decterov S. Thermodynamic modelling of the Al2O3 – CaO – FeO – Fe2O3 – PbO – SiO2 – ZnO system with addition of K and Na with metallurgical applications. Santiago, Chile, 2009, pp. 473—490. Available at: https://pdfs.semanticscholar.org/0804/0a0bc1ea0e1f5a0ca22d7b78e3ad3e2a191d.pdf.

Шихта для изготовления алюможелезистой шпинели и огнеупоров с использованием алюможелезистой шпинели : пат. 105389 Россия : МПК С04 В 35/043. Аксельрод Л. М., Пицик О. Н., Киселева Е. А., Найман Д. А. ; заявитель и патентообладатель Общество с ограниченной ответственностью «Группа «Магнезит». № 2013159119/03 ; заявл. 30.12.2013 ; опубл. 20.02.2015 , Бюл. № 5.

Obshchestvo s ogranichennoy otvetstvennost'yu "Gruppa "Magnezit" [Limited Liability Company "Magnezit Group"]. Shikhta dlya izgotovleniya alyumozhelezistoy shpineli i ogneuporov s ispol'zovaniyem alyumozhelezistoy shpineli [Charge for manufacture of aluminum - ferrous spinel and refractory using aluminum - ferrous spinel]. Inventors: Aksel'rod L. M., Pitsik O. N., Kiseleva E. A., Najman D. A. Appl: 2013-30-12, no. 2013159119/03; publ: 2015-20-02, Bull. no. 5. IPC С04 В 35/043. Patent RF, no. 105389 (in Russian).

Герцинитсодержащие огнеупоры – перспективное направление в ассортименте продукции группы Mагнезит / Л. М. Аксельрод и др. Новые огнеупоры. 2016. № 3. С. 28.

Aksel'rod L. M., Turchin M. Yu., Yeroshin M. A., Pitsik O. N., Kiseleva Ye. A. Gertsinitsoderzhashchiye ogneupory – perspektivnoye napravleniye v assortimente produktsii gruppy Magnezit [Hercynite-containing refractory – a promising direction in the product range of the Magnesite group]. Novye ogneupory [New refractories]. 2016, no. 3, р. 28 (in Russian).

Разработка технологии изготовления и организация производства герцинита / Л. М. Аксельрод и др. Новые огнеупоры. 2016. № 3. С. 20.

Aksel'rod L. M., Nazmiyev M. I., Ilyankin A. V., Sementsov A. A., Gorodov A. A. Razrabotka tekhnologii izgotovleniya i organizatsiya proizvodstva gertsinita [Development of manufacturing technology and organization of the production of hercinitis]. Novye ogneupory [New refractories]. 2016, no. 3, р. 20 (in Russian).

Thermodynamic modelling of the Al2O3 – CaO – CoO – CrO – Cr2O3 – FeO – Fe2O3 – MgO – MnO – NiO – SiO2 – S system and applications in ferrous process metallurgy / S. A. Decterov et al. VII International Conference on Molten Slags Fluxes and Salts. The South African Institute of Mining and Metallurgy, 2004. P. 839—850. URL: https://www.pyrometallurgy.co.za/MoltenSlags2004/839-Decterov.pdf.

Decterov S. A., Jung I.-H., Jak E., Kang Y.-B., Hayes P., Pelton A. D. Thermodynamic modelling of the Al2O3 – CaO – CoO – CrO – Cr2O3 – FeO – Fe2O3 – MgO – MnO – NiO – SiO2 – S system and applications in ferrous process metallurgy. VII International Conference on Molten Slags Fluxes and Salts. The South African Institute of Mining and Metallurgy. 2004, рр. 839—850. Available at: https://www.pyrometallurgy.co.za/MoltenSlags2004/839-Decterov.pdf.

MgO saturation analysis of CaO – SiO2 – FeO – MgO – Al2O3 slag system / Rodolfo Arnaldo Montecinos de Almeidaa, Deisi Vieiraa, Wagner Viana Bielefeldtb, Antоnio Cezar Faria Vilelab. Materials Research. 2018. № 21 (1): e20170041. URL: http://www.scielo.br/pdf/mr/v21n1/1516-1439-mr-1980-5373-MR-2017-0041.pdf.

Rodolfo Arnaldo Montecinos de Almeidaa, Deisi Vieiraa, Wagner Viana Bielefeldtb, Antоnio Cezar Faria Vilelab. MgO saturation analisys of CaO – SiO2 – FeO – MgO – Al2O3 slag system. Materials Research. 2018, no. 21 (1): e20170041. Available at: http://www.scielo.br/pdf/mr/v21n1/1516-1439-mr-1980-5373-MR-2017-0041.pdf.

Строение системы CaO – MgO – Fe2O3 – Al2O3 в области субсолидуса / Я. Н. Питак и др. Збірник наукових праць ПАТ «УКРНДІ ВОГНЕТРИВІВ ІМ. А. С. БЕРЕЖНОГО». 2013. № 113. C. 65—70.

Pytak Ya. N., Peschanskaya V. V., Pytak O. Ya., Yuzenko N. A., Dubovys V. H. Stroenye systemy CaO – MgO – Fe2O3 – Al2O3 v oblasty subsolydusa [The structure of the CaO – MgO – Fe2O3 – Al2O3 system in the region of the subsolidus]. Zb. nauk. pr. PAT "UKRNDI VOGNETRYVIV IM. A. S. BEREZHNOGO" [Coll. Sci. Proc. of PJSC "THE URIR NAMED AFTER A. S. BEREZHNOY"]. Kharkov, PAT "UKRNDI VOGNETRYVIV IM. A. S. BEREZHNOGO" Publ., 2013, no. 113, рр. 65—70. (in Russian).

Viscosity and structure evolution of the SiO2 – MgO – FeO – CaO – Al2O3 slag in ferronickel smelting process from laterite / X.-M. Lv et al. Journal of Mining and Metallurgy, Section B: Metallurgy. 2017. № 53 (2). Р. 147—154. URL: http://www.doiserbia.nb.rs/img/doi/1450-5339/2017/1450-53391700002L.pdf.

Lv X.-M., Lv X.-W., Wang L.-W., Qiu J., Liu M. Viscosity and structure evolution of the SiO2 – MgO – FeO – CaO – Al2O3 slag in ferronickel smelting process from laterite. Journal of Mining and Metallurgy, Section B: Metallurgy. 2017, no. 53 (2), рр. 147—154. Available at: http://www.doiserbia.nb.rs/img/doi/1450-5339/2017/1450-53391700002L.pdf.

Malcolm W. Chase, Jr. NIST - JANAF Thermochemical Tables. Fourth edition. Part 1, Al—Co. J. Phys. Chem. Ref. Data, Monograph 9. 61 p. / URL: https://janaf.nist.gov/pdf/JANAF-FourthEd-1998-1Vol1-Intro.pdf.

Malcolm W. Chase, Jr. NIST - JANAF Thermochemical Tables. Fourth edition. Part 1, Al—Co. J. Phys. Chem. Ref. Data, Monograph 9. 61 p. Available at: https://janaf.nist.gov/pdf/JANAF-FourthEd-1998-1Vol1-Intro.pdf.

Бабушкин В. И., Матвеев Г. М., Мчедлов – Петросян О. П. Термодинамика силикатов. Москва : Стройиздат, 1986. 408 с.

Babushkin V. I., Matveyev G. M., Mchedlov – Petrosyan O. P. Termodinamika silikatov [Thermodynamics of silicates]. Moscow, Stroyizdat Publ., 1986. 408 р. (in Russian).

Третьяков Ю. Д. Твердофазные реакции. Москва : Химия, 1978. 360 с.

Tret'yakov Yu. D. Tverdofaznye reaktsii [Solid - phase reactions]. Moscow, Khimiya Publ., 1978. 360 р. (in Russian).

Published
2020-12-30
How to Cite
Borysenko, O. M., Logvinkov, S. M., Shabanova, G. M., Korohodska, A. M., Ostapenko, I. A., & Ivashura, A. A. (2020). Thermodynamic studies in the MgO – FeO – Al2O3 system. Scientific Research on Refractories and Technical Ceramics, 120, 115-119. https://doi.org/10.35857/2663-3566.120.10