@article{Primachenko_Babkina_Khonchik_Nikulina_Tishina_Karyakina_2018, title={Effect investigation of the dispersion and type of fine-ground component, as well as the type of dispersing additives on the properties of low-cement periclase castable and samples from it}, volume={118}, url={https://refractories-journal-ua.com/index.php/journal/article/view/29}, DOI={10.35857/2663-3566.118.07}, abstractNote={<p>Researches have been carried out, as well as technological parameters have been developed for obtaining of low-cement periclase castable and products from it based on sintered periclase, periclase scrap, high alumina cement and dispersing additives. The possibility of using as cement brand of “VGTS-73” of own production of JSC&nbsp;“URIR named after A.&nbsp;S.&nbsp;Berezhnoy”, as well as cement Gorkal-70 (Poland) is established. The dispersion of fine-ground component of charge (mainly periclase and in a small amount of high alumina cement) and the possibility of using Castament FS-10 + Castament FW-10 (Germany), SioxX-Mag (Norway) and Lithopix P 5 (Germany) are established. Castament FS-10 + FW-10 and SioxX-Mag are more effective in terms of obtaining periclase castable products with better service properties. The temperature of thermal treatment of unburned products (350 <sup>о</sup>C), the firing temperature of products (~ 1450 <sup>о</sup>C) and the possible application temperature of fired products (1580 <sup>о</sup>C and above) are established.</p> <p>The developed low-cement periclase castables and samples from them are characterized, depending on the used dispersing additives, by the following indicators of physicochemical properties: content, wt.&nbsp;%: MgO — 85—86, SiO<sub>2</sub> — 2.0—6.0, CaO — 1.5—2.5, Fe<sub>2</sub>O<sub>3</sub> — not more than 2.0; grain composition, mm — 6—0; open porosity of the samples after thermal treatment at temperatures of 350 and 1450 <sup>о</sup>C is 20.3—23.0 and 18.8—22.8 %, respectively; apparent density of the samples after thermal treatment at temperatures of 350 and 1450 <sup>о</sup>C is 2.63—2.69 and 2.74—2.86 g/cm<sup>3</sup>, respectively; cold crushing strength of the samples after thermal treatment at 350, 1450 and 1580 <sup>о</sup>C — 19—38, 31—65 and 29—72 N/mm<sup>2</sup>, respectively; refractoriness under a load of 0.2 N/mm<sup>2</sup> of the samples after thermal treatment at 1450 <sup>о</sup>C is 1450—1470 <sup>о</sup>C.</p> <p>The developed low-cement periclase castables and products from them are recommended for service in the conditions, above all, the impact of basis slags. The manufacture of castables and products from them is mastered at the pilot production of JSC&nbsp;“URIR named after A.&nbsp;S.&nbsp;Berezhnoy”.</p&gt;}, journal={Scientific research on refractories and technical ceramics}, author={Primachenko, V. V. and Babkina, L. A. and Khonchik, I. V. and Nikulina, L. N. and Tishina, T. G. and Karyakina, E. L.}, year={2018}, month={Dec.}, pages={69-86} }