Creation of electrically conductive composite ceramics based on facing tiles with the addition of SiC
Abstract
In the article, the creation of electrically conductive composite ceramics based on facing tiles with the addition of SiC with specified electrodynamics’ characteristics was considered.
To obtain a press powder, the raw materials in a predetermined amount were weighed, 10, 20 and 30 % silicon carbide were added and subjected to wet grinding in a ball mill. The resulting slip was dried in a drying oven and passed through a № 05 sieve. The finished press powder for facing ceramics with SiC, moistened to 8 %, was weighed and poured into a mold for pressing, the pressure force was 18—20 MPa. The resulting green was dried in a drying oven. The semi-finished product was burned in a sillite furnace at a firing temperature of 1120—1140 °C with a holding at a maximum temperature of 5—10 minutes. The chemical composition of obtained press powder and the technological scheme for obtaining samples were presented.
The obtained data shown that the best sample was facing ceramics with 30 % SiC, which had the following properties: water absorption — 5.9 %, open porosity — 12.5 %, apparent density — 2.13 g/cm2, resistivity — 0.43 ⋅10-6 Ohm ⋅m. The obtained X-ray diffraction pattern indicated the presence of silicon carbide in the sample after firing, which was confirmed by the data on the study of specific volumetric resistance of the studied ceramics and the obtained practical results.
References
Шевель Д. М. Электромагнитная безопасность. Киев : Век+, НТИ, 2002. 432 с.
Shevel D. M. Elektromagnitnaya bezopasnost [Electromagnetic safety]. Kyiv, Vek+, NTI Publ., 2002. 432 p. (in Russian).
Давыдов Б. И., Тихончук В. С., Антипов В. В. Биологическое действие, нормирование и защита от электромагнитных излучений / под ред. Ю. Г. Григорьева. Москва : Энергоатомиздат, 1984. 176 с.
Grigorev Yu. G., ed. Davyidov B. I., Tihonchuk V. S., Antipov V. V. Biologicheskoe deystvie, normirovanie i zaschita ot elektromagnitnyih izlucheniy [Biological action, regulation and protection against electromagnetic radiation]. Moscow, Energoatomizdat Publ., 1984. 176 p. (in Russian).
Минин Б. А. СВЧ и безопасность человека. Москва : Советское радио, 1974. 352 с.
Minin B. A. SVCh i bezopasnost cheloveka [Microwave and human safety]. Moscow, Sovetskoe radio Publ., 1974. 352 p. (in Russian).
Іванов В. Г., Дзюндзюк Б. В., Олександров Ю. М. Охорона праці в електроустановках. Київ : АТ „Око”, 1994. 227 с.
Ivanov V. H., Dziundziuk B. V., Oleksandrov Yu. M. Okhorona pratsi v elektroustanovkakh [Occupational safety in electrical installations]. Kyiv, AT "Oko" Publ., 1994. 227 p. (in Ukrainian).
Нефедова А. Л., Сахацкий В. Д., Аль-Хеяри А., Нефедов Л. И. Анализ методов и средств защиты от электромагнитных полей. Науковий вісник будівництва. 1999. № 8. С. 193—202.
Nefedova A. L., Sahatskiy V. D., Al-Heyari A., Nefedov L. I.. Analiz metodov i sredstv zaschityi ot elektromagnitnyih poley [Analysis of methods and means of protection against electromagnetic fields]. Naukovyi visnyk budivnytstva [Scientific Bulletin of Construction]. 1999, no.8, pp. 193—202 (in Russian).
Крылов В. А., Юченкова Т. В. Защита от электромагнитных излучений. Москва : Советское радио, 1972. 216 с.
Kryilov V. A., Yuchenkova T. V. Zaschita ot elektromagnitnyih izlucheniy [Protection against electromagnetic radiation]. Moscow, Sovetskoe radio Publ., 1972. 216 p. (in Russian).
Воробьев Е. А. Экранирование СВЧ конструкций. Москва : Советское радио, 1979. 136 с.
Vorobev E. A. Ekranirovanie SVCh konstruktsiy [Shielding of microwave structures]. Moscow, Sovetskoe radio Publ., 1979. 136 p. (in Russian).
Петров В. М., Гагулин В. В. Радиопоглощающие материалы. Неорганические материалы. 2001. Т. 37, № 2. С. 135—141.
Petrov V. M., Gagulin V. V. Radiopogloschayuschie materialyi [Radiopaque materials]. Neorganicheskie materialyi [Inorganic materials]. 2001, vol. 37, no. 2, pp. 135—141 (in Russian).
Левин Б. Е., Третьяков Ю. Д., Летюк Л. М. Физико-химические основы получения, свойства и применения ферритов. Москва : Металлургия, 1979. 472 с.
Levin B. E., Tretyakov Yu. D., Letyuk L. M. Fiziko-himicheskie osnovyi polucheniya, svoystva i primeneniya ferritov [Physicochemical bases of production, properties and use of ferrites]. Moscow, Metallurgiya Publ., 1979. 472 p. (in Russian).
Влияние токопроводящих добавок на электрофизические свойства облицовочной керамики / Г. В. Лисачук и др. Вісник Національного технічного університету “Харківський політехнічний інститут”. 2005. № 25. С. 163—166.
Lisachuk G. V. et al. Vliyanie tokoprovodyaschih dobavok na elektrofizicheskie svoystva oblitsovochnoy keramiki [Influence of conductive additives on the electrical properties of facing ceramics]. Visnyk NTU ″KhPI″ [Bulletin of the National Technical University ″KhPI″]. Kharkiv, NTU ″KhPI″ Publ., 2005, no. 25, pp. 163—166 (in Russian).
Разработка композиционных покрытий по керамике, экранирующих электромагнитные излучения / Г. В. Лисачук и др. Вестник науки и техники. 2005. № 4 (23). С. 55—60.
Lisachuk G. V. et al. Razrabotka kompozitsionnyih pokryitiy po keramike, ekraniruyuschih elektromagnitnyie izlucheniya [Development of composite coatings for ceramics, shielding electromagnetic radiation]. Vestnik nauki i tehniki [Bulletin of Science and Technology]. Kharkiv, NTU ″KhPI″ Publ., 2005, no. 4 (23), pp. 55—60 (in Russian).
Получение полупроводящих облицовочных керамических материалов, экранирующих ЭМИ / Г. В. Лисачук и др. Технология и применение огнеупоров и технической керамики в промышленности : междунар. науч.-техн. конф., Харьков, 26—27 апр. 2005 г. : тез. докл. Харьков : Каравелла, 2005. С. 54.
Lisachuk G. V., Shchukina L. P., Krivobok R. V., Emaeva O. A., Rad'kova E. A., Tsapko N. S. Poluchenie poluprovodyaschih oblitsovochnyih keramicheskih materialov, ekraniruyuschih EMI [Obtaining semiconducting ceramic facing materials, shielding EMI]. Tekhnologiya i primeneniye ogneuporov i tekhnicheskoy keramiki v promyshlennosti. Tezisy dokladov mezhdunarodnoy nauchno-teknicheskoy konferencii (26—27 Apr. 2005, Kharkiv) [Technology and application refractories and technical ceramics in industry. Abstracts of Int. Sci.-Techn. Conf. (26—27 Apr. 2005, Kharkiv)]. Kharkiv, Karavela Publ., 2005, pp. 54 (in Russian).
Литвиненко Е. А., Дзюндзюк Б. В., Халимон И. И. Защита от электромагнитных полей. Киев : УкрНИИНТИ, 1971. 33 с.
Litvinenko E. A., Dzyundzyuk B. V., Halimon I. I. Zaschita ot elektromagnitnyih poley [Protection against electromagnetic fields]. Kyiv, UkrNIINTI Publ., 1971. 33 p. (in Russian).
Ковнеристый Ю. К., Лазарева И. Ю., Раваев А. А. Материалы, поглощающие СВЧ-излучения. Москва : Наука, 1982. 165 с.
Kovneristyiy Yu. K., Lazareva I. Yu., Ravaev A. A. Materialyi, pogloschayuschie SVCh-izlucheniya [Microwave absorbing materials]. Moscow, Nauka Publ., 1982. 165 p. (in Russian).
Electromagnetic wave absorber of silicon carbide fibers : пат. 4507354 США : МПК B 32 B 7/00. № 477249 ; заявл. 21.03.83 ; опубл. 26.03.85, Бюл. № 6. 6 с.
Electromagnetic wave absorber of silicon carbide fibers. Appl: 1983-03-21, no. 477249; publ: 1985-03-26. IPC B 32 B 7/00. Patent USA no. 4507354. Bul. no. 6. 6 p.
Влияние магнитных и немагнитных добавок на свойства облицовочной керамики / Г. В. Лисачук и др. Вісник Національного технічного університету «Харківський політехнічний інститут». 2005. № 51. С. 168—173.
Lisachuk G. V. et al. Vliyanie magnitnyih i nemagnitnyih dobavok na svoystva oblitsovochnoy keramiki [Influence of magnetic and non-magnetic additives on the properties of facing ceramics]. Visnyk NTU ″KhPI″ [Bulletin of the National Technical University ″KhPI″]. Kharkiv, NTU ″KhPI″ Publ., 2005, no. 51, pp. 168—173 (in Russian).
This work is licensed under a Creative Commons Attribution 4.0 International License.