Influence research of an α–form alumina type on the properties of samples from vibrocasting mullite corundum granular masses

  • V. V. Martynenko JSC "URIR named after A. S. Berezhnoy", Kharkov, Ukraine
  • P. A. Kushchenko JSC "URIR named after A. S. Berezhnoy", Kharkov, Ukraine
  • I. G. Shulyk JSC "URIR named after A. S. Berezhnoy", Kharkov, Ukraine
  • K. I. Kushchenko JSC "URIR named after A. S. Berezhnoy", Kharkov, Ukraine
  • Yu. O. Krakhmal JSC "URIR named after A. S. Berezhnoy", Kharkov, Ukraine
  • L. P. Tkachenko JSC "URIR named after A. S. Berezhnoy", Kharkov, Ukraine
Keywords: vibrocasting, mullite corundum crucibles, alumina, dispersion.

Abstract

The technology of refractories vibrocasting was developed by JSC "URIR named after A. S. Berezhnoy" in particular highly refractory mullite corundum crucibles for melting of heat-resistant alloys in induction furnaces. At manufacturing of highly refractory vibrocasting mullite corundum refractories a-form alumina, as a dispersion binder, which milling to a particles size of less than 10 μm (the content of particles less than 4 μm in such alumina is more than 50 %) is used. For improvement the casting characteristics of vibrocasting masses dispersants are used. At research milling kinetics alumina of all brands was milling in a vibration mill for a specified time. For this research a certain amount of the investigated alumina of each brand was loaded into a vibration mill, and after a specified grinding time (30, 45, 60, 75 and 90 min), a sample of alumina after milling was taken in a specified amount. In this work, the kinetics of changes the dispersion of alumina (S, N and NR brands) during their milling was studied. The dispersion of alumina which were needed (the content of particles less than < 10 μm in such alumina is not less than 90 %, the content of particles less than < 4 μm — not less than 50 %) was achieved in almost the same milling time was found (~ 45 min). With a further increase of milling time to 60, 75 and 90 minutes, the dispersion of alumina N and NR brands increases in comparison with alumina S brand and after 90 minutes of milling, the content of particles < 4 μm in alumina, respectively, is ~ 60, ~ 75 and ~ 80 %. After fired at a temperature of 1580 °C the properties of vibrocasting mullite corundum samples, which contain alumina S, N and NR brands, are characterized by a high level of apparent density (above 3 g/cm3), open porosity (less than 16 %) and cold crushing strength (above 140 N/mm2). The high properties make it possible to use a-form alumina N and NR brands along a-form alumina S brand in the technology of vibrocasting mullite corundum refractories, including the highly refractory mullite corundum crucibles.

References

Примаченко В. В. Исследования по разработке новой технологии производства крупногабаритных изделий методом вибролитья из зернистых масс. Повышение качества и стойкости огнеупоров в тепловых агрегатах и снижение их расхода в народном хозяйстве : Всесоюзная науч.–техн. конф. : тез. докл. М. : Черметинформация, 1977. С. 36—37.

Primachenko V. V. Issledovaniya po razrabotke novoy tehnologii proizvodstva krupnogabaritnyih izdeliy metodom vibrolitya iz zernistyih mass The research on the development of a new technology manufacture of large-sized products by vibrocast method from grainy masses. Povyishenie kachestva i stoykosti ogneuporov v teplovyih agregatah i snizhenie ih rashoda v narodnom hozyaystve. Tezisy dokladov Vsesoyuznoy nauchno- teknicheskoy konferencii [Improving the quality and resistance of refractories in thermal units and reducing their consumption in the national economy. Abstracts of the All-Union Sci.-Techn. Conf.]. Moscow, Chermetinformatsiya Publ. [Chermetinformation], 1977, pp. 36—37 (in Russian).

Исследования по изготовлению крупногабаритных алюмосиликатных огнеупоров способом вибролитья / B. B. Примаченко и др. Тематич. отрасл. сб. «Производство специальных огнеупоров». М. : Металлургия, 1978. № 6. С. 58—62.

Primachenko V. V., Pitak N. V., Kolesnikov L. M., Zadorozhnaya T. A. Issledovaniya po izgotovleniyu krupnogabaritnyih alyumosilikatnyih oneuporov sposobom vibrolitya [The research on the manufacture of large-sized aluminosilicate by vibrocast method] Tematich. otrasl. sb. "Proizvodstvo spetsialnyih ogneuporov" [Thematic. Indust. Coll. "Production of special refractories"]. Moscow, Metallurgiya Publ. [Metallurgy], 1978, no. 6, pp. 58—62 (in Russian).

Исследование муллитокорундовых стаканов после службы при плавке в вакууме сплавов на никелевой основе / В. В. Примаченко и др. Огнеупоры. 1980. № 6. С. 18—19.

Primachenko V. V., Ustichenko V. V., Zhukova Z. D., Gladkov V. A., Lapin A. M., Kasatkin Yu. T. Issledovanie mullitokorundovyih stakanov posle sluzhbyi pri plavke v vakuume splavov na nikelevoy osnove The research of mullitecorundum crucible after exploitation in vacuum melting of nickelbased alloys Ogneupory Refractories. 1980, no. 6, pp. 18—19 (in Russian).

Примаченко В. В., Колесников Л. М., Устиченко В. А. Новые эффективные футеровки индукционных тигельных печей для плавки специальных сталей и сплавов. Темач. отрасл. сб. Украинского гос. науч.–исследоват. ин–та огнеупоров. Харьков, 1993. С. 123—129.

Primachenko V. V., Kolesnikov L. M., Ustichenko V. V. Novyie effektivnyie futerovki induktsionnyih tigelnyih pechey dlya plavki spetsialnyih staley i splavov New efficient linings for induction crucible furnaces for melting special steels and alloys Temach. otrasl. sb. Ukrainskogo gos. nauchno–issledovat. in–ta ogneuporov Thematic. Indust. Coll. Ukrainian state Research Institute of Refractories. Kharkiv, 1993, pp. 123—129 (in Russian).

Примаченко В. В., Устиченко В. А., Коровянская А. А. О технологии изготовления муллитокорундовых тиглей. Огнеупоры. 1990. № 3. С. 24—29.

Primachenko V. V., Ustichenko V. V., Korovyanskaya A.A. O tehnologii izgotovleniya mullitokorundovyih tigley About the technology of manufacturing mullitecorundum crucibles Ogneupory Refractories. Moscow, 1990, no. 3, pp. 24—29 (in Russian).

Примаченко В. В. Физико-химические основы и новая технология производства крупногабаритных огнеупоров — вибролитье : дис. … доктора техн. наук : 05.17.11 / Украинский научно–исследовательский институт огнеупоров. Харьков, 1995. 419 с.

Primachenko V. V. Fiziko–-himicheskie osnovyi i novaya tehnologiya proizvodstva krupnogabaritnyih ogneuporov — vibrolite : dis. … d-ra tekhn. nauk 05.17.11 Physicochemical fundamentals and new technology for the production of large-sized refractories — vibrocasting. Dr. eng. sci. diss. Ukrainian Research Institute of Refractories. Kharkov, 1995. 419 p. (in Russian).

Primachenko V., Ustichenko V., Chaplianko S. Corundum based crucibles for induction melting of heatresistant alloys. Stall und Eisen. Düsseldorf : Verlag Stahleisen GmbH., 2006. Р. 52—54.

Primachenko V., Ustichenko V., Chaplianko S. Corundum based crucibles for induction melting of heatresistant alloys. Stall und Eisen. Düsseldorf, Verlag Stahleisen GmbH., 2006, pp. 52—54 (in English).

Вибролитые тигли различного состава для индукционной плавки жаропрочных сплавов / В. В. Примаченко и др. Литье и металлургия. Спецвыпуск. Минск : Беларуcкий национальный технический университет, 2012. 3(67). С. 169—171.

Primachenko V. V., Martynenko V. V., Shulik I. G., Chaplianko S. V. Gritsyuk L. V., Tkachenko L. P. Vibrolityie tigli razlichnogo sostava dlya induktsionnoy plavki zharoprochnyih splavov The crucibles from different compositions by vibrocasting for induction melting of heat-resistant alloys Lite i metallurgiya. Spetsvyipusk Casting and metallurgy. Special issue. Minsk, Belaruckiy natsional'nyy tekhnicheskiy universitet Publ. [Belarusian National Technical University], 2012, no. 3(67), pp. 169—171 (in Russian).

Примаченко В. В. Вибролитье огнеупоров : избранные научные труды в 2 томах. Харьков : Точка, 2020. Т. ІІ. 510 с.

Primachenko V. V. Vibrolite ogneuporov: izbrannyie nauchnyie trudyi v 2 tomah Vibrocasting of refractories. Selected scientific works in 2 volumes. Kharkov, Tochka Publ, 2020, V. II, 419 p. (in Russian).

Зависимость свойств вибролитой муллитокорундовой массы и образцов из нее от вида и количества активного глинозема / В. В. Примаченко и др. Зб. наук. пр. ПАТ «УКРНДІВОГНТРИВІВ ІМЕНІ А. С. БЕРЕЖНОГО». Харьков : ПАТ «УКРНДІ ВОГНТРИВІВ ІМЕНІ А. С. БЕРЕЖНОГО», 2016. № 116. С. 11—18.

Primachenko V. V. Zavisimost svoystv vibrolitoy mullitokorundovoy massy i obraztsov iz nee ot vida i kolichestva aktivnogo glinozema [Dependence of the properties of vibrocast mullitecorundum mass and samples from it on the type and amount of active alumina]. Zb. nauk. pr. PAT "UKRNDI VOGNETRYVIV IM. A. S. BEREZhNOGO" [Coll. Sci. Proc. of PJSC "THE URIR NAMED AFTER A. S. BEREZHNOY"]. Kharkov, PAT "UKRNDI VOGNETRYVIV IM. A. S. BEREZhNOGO" Publ., 2016, no. 116, pp. 11—18 (in Russian).

Published
2020-12-30
How to Cite
Martynenko, V. V., Kushchenko, P. A., Shulyk, I. G., Kushchenko, K. I., Krakhmal, Y. O., & Tkachenko, L. P. (2020). Influence research of an α–form alumina type on the properties of samples from vibrocasting mullite corundum granular masses. Scientific Research on Refractories and Technical Ceramics, 120, 39-51. https://doi.org/10.35857/2663-3566.120.04

Most read articles by the same author(s)